Corrosion protection of AA6061-T4 alloy by sol-gel derived micro and nano-scale hydroxyapatite (HA) coating


Sonmez S., AKSAKAL B., Dikici B.

JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY, cilt.63, sa.3, ss.510-518, 2012 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 63 Sayı: 3
  • Basım Tarihi: 2012
  • Doi Numarası: 10.1007/s10971-012-2813-8
  • Dergi Adı: JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.510-518
  • Atatürk Üniversitesi Adresli: Hayır

Özet

Micron and nano-scale hydroxyapatite (HA) were coated successfully on AA6061-T4 substrates by sol-gel method. Besides, the effects of coating thickness on adhesion strength and corrosion behaviour of the coatings were studied. Corrosion resistance was measured by potentiodynamic polarization test using a potentiostat under in vitro conditions. The coatings before and after corrosion tests were characterized by adhesion tests, a scanning electron microscopy attached with EDS and X-ray diffraction analysis. The results revealed that all the coatings exhibit a passive behaviour in Ringer's solution. Specimens coated with nano-scale HA had the higher corrosion resistance than micro-scale coatings. The highest corrosion resistance appeared to be for the similar to 30 mu m nano-scale HA coated substrates. However, for micro-scale HA coatings, the highest adhesion resistance was obtained at similar to 30 mu m film thickness.