Microstructural Characterization and Wear Behavior of Porous Equimolar TiNbZr Medium-Entropy Alloys Scaffolds Produced by Mechanical Alloying

Creative Commons License

Karadeniz S., Arslan E.

MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS, cilt.25, 2022 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 25
  • Basım Tarihi: 2022
  • Doi Numarası: 10.1590/1980-5373-mr-2022-0238
  • Dergi Adı: MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, Aerospace Database, Communication Abstracts, Compendex, Metadex, Directory of Open Access Journals, Civil Engineering Abstracts
  • Anahtar Kelimeler: Equimolar TiNbZr alloy, Medium-entropy alloys, Porous scaffolds, Powder metallurgy, Mechanical property, Wear behavior, Cold isostatic press, Space-holder method, Ammoniumhydrogen carbonate (NH4HCO3), BIOCOMPATIBILITY, POROSITY
  • Atatürk Üniversitesi Adresli: Evet

Özet

Recently, there has been increasing importance on scaffold materials that could be used in biomaterials. In the present study, equimolar TiNbZr medium entropy alloys (MEAs) and porous TiNbZr alloy scaffolds were produced by mechanical alloying (MA) that is a powder metallurgy processing technique. The MA process was carried out using high energy planetary ball mill. Ammonium bicarbonate (NH4HCO3) at different percentage ratio was used as space holder to fabricate the porous TiNbZr scaffolds with using space-holder sintering method. Cold Isostatic Pressing (CIP) was performed for consolidation of mechanically alloyed powders. Finally, the green compact samples were sintered in tube furnace under vacuum atmosphere. The microstructural analyses, phase composition, porosity and density measurement, compression and microhardness tests and wear resistance of bulk alloys were examined. The X-Ray Diffraction (XRD) patterns of all samples indicated the dominant beta-Ti phases and small amount of alpha-Ti phase. SEM (scanning electron microscope) images for porous TiNbZr alloy scaffolds demonstrated that porosity increased with increase of space holders amount. With the increasing porosity content, density, hardness, compressive strength and the elastic modulus of samples decreased while wear rate increased.