Structural, Optical and Electrochromic Properties of WO3 Thin Films Prepared by Chemical Spray Pyrolysis Versus Spin Coating Technique


MORKOÇ KARADENİZ S., TATAR D., ERTUĞRUL M., EKİNCİ A. E.

SPECTROSCOPY AND SPECTRAL ANALYSIS, cilt.38, sa.9, ss.2982-2988, 2018 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 38 Sayı: 9
  • Basım Tarihi: 2018
  • Doi Numarası: 10.3964/j.issn.1000-0593(2018)09-2982-07
  • Dergi Adı: SPECTROSCOPY AND SPECTRAL ANALYSIS
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.2982-2988
  • Anahtar Kelimeler: Spray pyrolysis, Spin coating, WO3, TUNGSTEN-OXIDE FILMS, HYDROTHERMAL SYNTHESIS, DEVICES, POWDER
  • Atatürk Üniversitesi Adresli: Evet

Özet

In this study, Tungsten Oxide (WO3) thin films were prepared by Chemical Spray Pyrolysis (CSP) and Spin Coating (SC) techniques and it was investigated effects of technique and parameter on the films. WO3 thin films were deposited on ITO (Indium Tin Oxide) coated glasses. The structural, optical and electrochromic properties of the WO3 thin films were characterized by XRD, SEM, UV, and CV measurements. The sharpest (200) peak was observed in the XRD spectra and optical band gaps were calculated around 2.6 similar to 3.1 eV via UV-Vis spectra for all of the samples. Micro fibrous reticulated surface (filamentous like) morphology for the films deposited by CSP technique and smooth surface morphology with high optical transmittance for the film deposited by SC Technique were obtained from SEM images. In addition to these results, it was revealed that all the samples exhibit good electrochromic performance.