Influence of plasma nitriding treatment on the adhesion of DLC films deposited on AISI 4140 steel by PVD magnetron sputtering


KOVACI H., BARAN Ö., BAYRAK Ö., Yetim A. F., ÇELİK A.

JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, cilt.31, sa.18, ss.2015-2027, 2017 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 31 Sayı: 18
  • Basım Tarihi: 2017
  • Doi Numarası: 10.1080/01694243.2017.1293923
  • Dergi Adı: JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.2015-2027
  • Anahtar Kelimeler: DLC, plasma nitriding, duplex treatment, adhesion, residual stress, WEAR PROPERTIES, ION-IMPLANTATION, SCRATCH ADHESION, FATIGUE-STRENGTH, CARBON-FILMS, ALLOY-STEEL, COATINGS, FRICTION, BEHAVIOR, MICROSTRUCTURE
  • Atatürk Üniversitesi Adresli: Evet

Özet

Duplex surface treatments composed of diamond like carbon (DLC) coating followed by plasma nitriding have drawn attention for a while. In this study, AISI 4140 steel substrates were plasma nitrided at different treatment temperatures and times. Then, DLC films were deposited on both untreated and plasma nitrided samples using PVD magnetron sputtering. The effect of different plasma nitriding temperatures and times on the structural, mechanical and adhesion properties of DLC coatings was investigated by XRD, SEM, microhardness tester and scratch tester, respectively. It was found that surface hardness, intrinsic stresses, layer thickness values and phase distribution in modified layers and DLC coating were the main factors on adhesion properties of duplex coating system. The surface hardness and residual stress values of AISI 4140 steel substrates significantly increased with both DLC coating and duplex surface treatment (plasma nitriding+DLC coating). Increasing plasma nitriding temperature and time also increased the diffusion depth and the thickness of modified layers. Hard surface layers led to a significant improvement on load bearing capacity of the substrate material. However, it was also determined that the process parameters, which provided lower intrinsic stresses, improved the adhesion properties of the duplex coating system.