Investigation of the usage possibility of CuO and CuS thin films produced by successive ionic layer adsorption and reaction (SILAR) as solid lubricant


KOVACI H., AKALTUN Y., Yetim A. F., Uzun Y., ÇELİK A.

Surface and Coatings Technology, cilt.344, ss.522-527, 2018 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 344
  • Basım Tarihi: 2018
  • Doi Numarası: 10.1016/j.surfcoat.2018.03.077
  • Dergi Adı: Surface and Coatings Technology
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.522-527
  • Anahtar Kelimeler: CuO, CuS, Solid lubricant, SILAR, Wear, WEAR BEHAVIOR, FRICTION, OXIDE, MICROSTRUCTURE, DEPOSITION, RESISTANCE, CORROSION, COATINGS, PTFE
  • Atatürk Üniversitesi Adresli: Evet

Özet

© 2018 Elsevier B.V.CuO and CuS films were coated on AISI 4140 steel samples by Successive Ionic Layer Adsorption and Reaction (SILAR) to investigate their usability as solid lubricant. Wear tests were performed using pin-on-disk tribo-tester under dry and lubricated conditions. The structural, morphological and morphological features of untreated, CuO and CuS coated samples were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM) and microhardness, scratch analysis. The surface examinations indicated that needle-like structures formed after coating processes and CuO and CuS films exhibited oleophobic behavior. CuO and CuS thin films reduced the coefficient of friction due to the low shear strength of bonding in transfer films. CuO and CuS films decreased the wear rates in comparison to untreated sample for both dry and lubricated conditions. Also, CuO thin films exhibited better wear resistance than CuS films in dry and lubricated wear tests. The overall results revealed that both CuO and CuS films produced by SILAR can be an alternative to conventional solid lubricants.