The effect of heat treatments applied to superstructure porcelain on the mechanical properties and microstructure of lithium disilicate glass ceramics

ÖZDEMİR H., ÖZDOĞAN A.

DENTAL MATERIALS JOURNAL, cilt.37, sa.1, ss.24-32, 2018 (SCI-Expanded) identifier identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 37 Sayı: 1
  • Basım Tarihi: 2018
  • Doi Numarası: 10.4012/dmj.2016-365
  • Dergi Adı: DENTAL MATERIALS JOURNAL
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.24-32
  • Anahtar Kelimeler: Lithium disilicate glass ceramic, Heat treatment, Microstructure, Mechanical properties, DENTAL PORCELAIN, SURFACE-ROUGHNESS, IN-VITRO, STRENGTH, WEAR, ZIRCONIA, FIRINGS, ENAMEL, COLOR, GLAZE
  • Atatürk Üniversitesi Adresli: Evet

Özet

The aim of this study was to investigate that heat treatments with different numbers applied to superstructure porcelain whether effects microstructure and mechanical properties of lithium disilicate ceramic (LDC). Eighty disc-shaped specimens were fabricated from IPS e.max Press. Specimens were fired at heating values of porcelain in different numbers and divided four groups (n=5). Initial Vickers hardness were measured and X-ray diffraction (XRD) analysis was performed. Different surface treatment were applied and then Vickers hardness, surface roughness and environmental scanning electron microscopy (ESEM) analysis were performed. Data were analyzed with Varyans analysis and Tukey HSD test (alpha=0.05). Initial hardness among groups was no significant different (p>0.05), but hardness and surface roughness after surface treatments were significant different (p<0.05). Lithium disilicate (LD) peaks decrease depended on firing numbers. ESEM observations showed that firing number and surface treatments effect microstructure of LDC. Increasing firing numbers and surface treatments effect the microstructure of LDC.