Corrosion and tribocorrosion properties of duplex surface treatments consisting of plasma nitriding and DLC coating


Kovaci H., BOZKURT Y. B., Yetim A. F., Baran O., Celik A.

TRIBOLOGY INTERNATIONAL, cilt.156, 2021 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 156
  • Basım Tarihi: 2021
  • Doi Numarası: 10.1016/j.triboint.2020.106823
  • Dergi Adı: TRIBOLOGY INTERNATIONAL
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, Academic Search Premier, Aerospace Database, Applied Science & Technology Source, Chimica, Communication Abstracts, Compendex, Computer & Applied Sciences, INSPEC, Metadex, Civil Engineering Abstracts
  • Anahtar Kelimeler: DLC, Plasma nitriding, Wear, Tribocorrosion
  • Atatürk Üniversitesi Adresli: Evet

Özet

In this study, a comprehensive analysis was performed to investigate the corrosion and tribocorrosion behaviour of untreated and duplex ceramic coated AISI 4140 steel. Therefore, samples were plasma nitrided in a glow discharge environment and then, they were coated with diamond-like carbon (DLC) film. Electrochemical impedance spectroscopy, potentiodynamic polarization and tribocorrosion tests were performed in fourteen different parameters. Nitriding treatment increased the surface roughness compared to the base material. The negative effect of roughness on corrosion and tribocorrosion performance has disappeared with the ceramic film thickness increasing with temperature and time. Harder surfaces compared to the base material contributed to the wear resistance. Compound, diffusion layers and DLC film have a barrier effect, delaying the arrival of the corrosive liquid to the base material.