TRIBOLOGICAL PROPERTIES OF TiO2/SiO2 DOUBLE LAYER COATINGS DEPOSITED ON CP-Ti
SURFACE REVIEW AND LETTERS, cilt.24, sa.6, 2017 (SCI-Expanded, Scopus)
- Yayın Türü: Makale / Tam Makale
- Cilt numarası: 24 Sayı: 6
- Basım Tarihi: 2017
- Doi Numarası: 10.1142/s0218625x17500822
- Dergi Adı: SURFACE REVIEW AND LETTERS
- Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
- Anahtar Kelimeler: Double layer coating, sol-gel, wear, scratch, Cp-Ti, MECHANICAL-PROPERTIES, TI-6AL-4V ALLOY, STAINLESS-STEEL, SCRATCH TEST, WEAR, FILM, RESISTANCE, ADHESION, TITANIUM, BEHAVIOR
- Atatürk Üniversitesi Adresli: Evet
Özet
In the present paper, the influences of different double layer on wear and scratch performances of commercially pure Titanium (CP-Ti) were investigated. TiO2/SiO2 and SiO2/TiO2 double layer coatings were deposited on CP-Ti by sol-gel dip coating process and calcined at 750 degrees C. The phase structure, cross-sectional morphology, composition, wear track morphologies, adhesion properties, hardness and roughness of uncoated and coated samples were characterized with X-ray diffraction, scanning electron microscopy (SEM), nano-indentation technique, scratch tester and 3D profilometer. Also, the tribological performances of all samples were investigated by a pin-on-disc tribotester against Al2O3 ball. Results showed that hardness, elastic modulus and adhesion resistance of double layer coated samples were higher than untreated CP-Ti. It was found that these properties of TiO2/SiO2 double layer coatings have higher than SiO2/TiO2 double layer coating. Additionally, the lowest friction coefficient and wear rates were obtained from TiO2/SiO2 double layer coatings. Therefore, it was seen that phase structure, hardness and film adhesion are important factors on the tribological properties of double layer coatings.