Catalytic Hydrolysis of Ammonia Borane via Cobalt Palladium Nanoparticles

Sun D., Mazumder V., Metin O., Sun S.

ACS NANO, cilt.5, sa.8, ss.6458-6464, 2011 (SCI-Expanded) identifier identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 5 Sayı: 8
  • Basım Tarihi: 2011
  • Doi Numarası: 10.1021/nn2016666
  • Dergi Adı: ACS NANO
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.6458-6464
  • Anahtar Kelimeler: ammonia borane hydrolysis, bimetallic nanoparticles, cobalt-palladium alloy catalyst, heterogeneous catalysis, hydrogen storage, MONODISPERSE NICKEL NANOPARTICLES, HYDROGEN GENERATION SYSTEM, DEHYDROGENATION, NANOCLUSTERS, STORAGE, DISSOCIATION
  • Atatürk Üniversitesi Adresli: Evet

Özet

Monodisperse 8 nm CoPd nanoparticles (NPs) with controlled compositions were synthesized by the reduction of cobalt acetylacetonate and palladium bromide in the presence of oleylamine and trioctylphosphine. These NPs were active catalysts for hydrogen generation from the hydrolysis of ammonia borane (AB), and their activities were composition dependent. Among the 8 nm CoPd catalysts tested for the hydrolysis of AB, the Co35Pd65 NPs exhibited the highest catalytic activity and durability. Their hydrolysis completion time and activation energy were 5.5 min and 27.5 kJ mol(-1), respectively, which were comparable to the best Pt-based catalyst reported. The catalytic performance of the CoPd/C could be further enhanced by a preannealing treatment at 300 degrees C under air for 15 h with the hydrolysis completion time reduced to 3.5 min. This high catalytic performance of Co35Pd65 NP catalyst makes it an exciting alternative in pursuit of practical implementation of AB as a hydrogen storage material for fuel cell applications.