Wear Behavior of Plasma Oxidized CoCrMo Alloy under Dry and Simulated Body Fluid Conditions


ÇELİK A., Aslan M., Yetim A. F., BAYRAK O.

JOURNAL OF BIONIC ENGINEERING, cilt.11, sa.2, ss.303-310, 2014 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 11 Sayı: 2
  • Basım Tarihi: 2014
  • Doi Numarası: 10.1016/s1672-6529(14)60035-4
  • Dergi Adı: JOURNAL OF BIONIC ENGINEERING
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.303-310
  • Anahtar Kelimeler: plasma oxidation, wear, CoCrMo, simulated body fluid, implant material, TRIBOLOGICAL PROPERTIES, ORTHOPEDIC MATERIALS, TI6AL4V ALLOY, MICROSTRUCTURE, CORROSION
  • Atatürk Üniversitesi Adresli: Evet

Özet

In this study, CoCrMo alloy was oxidized in plasma environment at the temperatures of 600 degrees C to 800 degrees degrees C for 1 h to 5 h with 100% O-2 gas and its tribological behavior was investigated. After the plasma oxidizing process, the compound and diffusion layers were formed on the surface. XRD results show that Cr2O3, alpha-Co and epsilon-Co phases diffracted from the modified layers after plasma oxidizing. The untreated and treated CoCrMo samples were subjected to wear tests both in dry and simulated body fluid conditions, and normal loads of 2 N and 10 N were used. For the sliding wear test, alumina balls were used as counter materials. It was observed that the wear resistance of CoCrMo alloy was increased after the plasma oxidizing process. The lowest wear rate was obtained from the samples that were oxidized at 800 degrees C for 5 h. It was detected that both wear environment and load have significant effects on the wear behavior of this alloy, and the wear resistance of oxidized CoCrMo alloy is higher when oxide-based counterface is used. The wear rates of both untreated and plasma oxidized samples increase under high loads.