ACTA PHYSICA POLONICA A, cilt.126, ss.782-786, 2014 (SCI-Expanded)
Bismuth (Bi) doped zinc oxide (ZnO:Bi) thin films were prepared on glass substrates by sol gel spin coating technique using homogeneous precursor solutions, and effects of Bi doping on the structural and optical properties of ZnO were investigated. The crystalline of ZnO films shifted from polycrystalline nature to amorphous nature with Bi doping. The plane stresses (a) for hexagonal ZnO and ZnO:Bi crystals were calculated according to the biaxial strain model. The Urbach rule was studied as a function of non-thermal component to the disorder (defects in crystal structures) which is especially observed in the case of non-crystal semiconductors. The calculated Urbach energies and steepness parameters of undoped ZnO and ZnO:Bi films varied between 44.33 meV and 442.67 meV, and 58.3 x 10(-2) and 5.8 x 10(-2), respectively. The Urbach energies of the films increased with an increase in the Bi doping concentration and a great difference was observed for 7.0 mol.% doping. The band gap values of the films exhibited a fluctuated behavior as a result of doping effect.