AIP Conference Proceedings, cilt.1833, ss.20092, 2017 (SCI-Expanded)
In our study, as p-type crystalline Si substrate was used. Omic contact was performed by evaporating Al metal on the matt surface of crystal. On the other surface of it CdS thin film were enlarged with the technique of Spray Pyrolysis. Structural characteristics of the grown thin film was examined SEM and EDAX image. When examining SEM image of CdS thin film were totally covered the p-Si crystal surface of it was nearly homogeneous and The EDAX spectra showed that the expected different ratios metal percent exist in the alloys, approximately. On the CdS films whose surface features were investigated, at 10(-7) torr pressure was obtained Cd/CdS/p-Si/Al sandwich structure by evaporating Cd. Firstly, the I-V (current-voltage) characteristics on 80K between 320K at room temperature of this structure was measured. I-V characteristics of the examined at parameters diodes calculation, Thermionic Emission, were used. The characteristic parameters such as barrier height and ideality factor of this structure have been calculated from the forward bias I-V characteristics. Consequently, it was seen that CdS thin film grown on p-Si semiconductor will be used confidently in Cd/p-Si metal-semiconductor contacts thanks to Spray Pyrolysis method.