Open Journal of Somatology, cilt.13, sa.4, ss.143-155, 2023 (Scopus)
The aim of this study is to investigate the color change of different restoration thicknesses, backgrounds and resin cement colors on lithium disilicate and zirconium reinforced lithium silicate materials in vitro. In this study, IPS emax CAD (LT C14) and Celtra Duo (LT C14) are used as full ceramic materials, and Variolink Esthetic LC (warm, neutral) used as resin cement and Tokuyama Estelite Sigma Quick (A3, A2) is used as composite materials. A total of 160 samples in the form of 40 pieces of 5 × 5 0.4 mm thick 40 pieces of 5 × 5 0.6 mm thick square discs from each of the all-ceramic materials in block form were obtained using a water jet device (DWJ1525-FA; Dardi International Corporation, Nanjing, China). Glass ceramic samples produced in 2 different thicknesses were cemented on 2 different backgrounds with 2 different resin types of cement. Color measurements of the samples before and after cementation were performed on a grey background with spectrophotometer Vita EasyShade V (Vita Zahnfabrik, Bad Sackingen, Germany) and color parameters (L*, a*, b*, ΔE) were calculated according to the CIE Lab (Commission Internationale de L’Eclairage) system. Average values for each group (ΔE) were not affected by ceramic type, material thickness, background color, resin cement color, and the interaction of these four variables (p > 0.05). When the triple interactions between the groups were examined, there were no statistically significant differences (p > 0.05). In the evaluation of pairwise interactions between two groups (material type-material thickness, material type-background color, and thickness of material-background interactions) statistically significant differences (p < 0.05) were seen. Clinical Implications: The material type, thickness, background and cement color used did not cause any statistically significant color change in lithium disilicate and zirconium-reinforced lithium silicate glass ceramic materials (p > 0.05).