Preparation of cetyltrimethylammonium bromide modified montmorillonite nanomaterial for adsorption of a textile dye

KIRANSAN M., SOLTANI R. D. C., HASSANI A., KARACA S., KHATAEE A.

JOURNAL OF THE TAIWAN INSTITUTE OF CHEMICAL ENGINEERS, cilt.45, sa.5, ss.2565-2577, 2014 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 45 Sayı: 5
  • Basım Tarihi: 2014
  • Doi Numarası: 10.1016/j.jtice.2014.06.007
  • Dergi Adı: JOURNAL OF THE TAIWAN INSTITUTE OF CHEMICAL ENGINEERS
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.2565-2577
  • Anahtar Kelimeler: Adsorption, Acid orange 7, Experimental design, Intercalation, Montmorillonite, Nano-clay, AQUEOUS-SOLUTIONS, METHYLENE-BLUE, CATIONIC DYE, ANIONIC DYE, ACID DYE, KINETICS, REMOVAL, OPTIMIZATION, THERMODYNAMICS, DECOLORIZATION
  • Atatürk Üniversitesi Adresli: Evet

Özet

The main aim of this investigation was to evaluate the efficacy of the cetyltrimethylammonium bromide (CTAB) modified montmorillonite (MMT) nanomaterial for the adsorption of Acid orange 7 (AO7) as an anionic dye in aqueous solutions. The decolorization efficiency (%) was first increased from 52.74% to 94.08% with increasing cation exchange capacity (CEC) from 0.5 to 1.0 CEC and then decreased to 74.89% with increasing the amount of added CTAB to 1.5 CEC. Response surface methodology (RSM) based on central composite design (CCD) was used to evaluate the effect of various operational parameters on the adsorption of AO7. Predicted values of decolorization efficiency were found to be in good agreement with obtained experimental values (R-2 = 0.9649). The maximum decolorization efficiency was predicted to be 87.19% at an AO7 concentration of 49 mg/L, adsorbent dosage of 0.8 g/L, reaction time of 27 min and initial pH of 6. The results of isotherm study fit the Freundlich model (R-2 > 0.9). Moreover, the adsorption of AO7 onto modified MMT was increased with increasing temperature which could be explained by the endothermic nature of the adsorption process. (C) 2014 Taiwan Institute of Chemical Engineers. Published by Elsevier B.V. All rights reserved.