Investigation of Corrosion Properties of LA-91 Alloy Coated with MAO Method

ŞÜKÜROĞLU S., TOTİK Y., ŞÜKÜROĞLU E. E., AVCİ S.

JOURNAL OF THE CHINESE SOCIETY OF MECHANICAL ENGINEERS, sa.2, ss.195-200, 2024 (SCI-Expanded) identifier

  • Yayın Türü: Makale / Tam Makale
  • Basım Tarihi: 2024
  • Dergi Adı: JOURNAL OF THE CHINESE SOCIETY OF MECHANICAL ENGINEERS
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, Aerospace Database, Communication Abstracts, Compendex, Metadex, Civil Engineering Abstracts
  • Sayfa Sayıları: ss.195-200
  • Atatürk Üniversitesi Adresli: Evet

Özet

LA91 magnesium alloy is a super lightweight magnesium -lithium alloy proposed for next generation materials. In addition to the advantages of these alloys such as low density, high strength-to -weight ratio, specific stiffness and brittleness, these alloys also have disadvantages such as low corrosion resistance and the oxide -carbonate film formed on the surfaces of the alloys cannot provide sufficient corrosion protection even in non-corrosive environments. In this study, micro arc oxidation, one of the coating methods, was applied to LA91 alloy. The surface morphologies of the coatings were characterized and it was aimed to increase the corrosion resistance of LA91 alloy. For this purpose, potentiodynamic polarization tests were carried out in 3.5% NaCl solution at room temperature to draw attention to the protection of the coating. As a result of the tests, it was determined that the oxide coatings raised on the surface